Double cross-linked polyetheretherketone proton exchange membrane for fuel cell
2012
Abstract The proton exchange membrane based on polyetheretherketone was prepared via two steps of cross-linking. The properties of the double cross-linked membrane (water uptake, proton conductivity, methanol permeability and thermal stability) have been investigated for fuel cell applications. The prepared membrane exhibited relatively high proton conductivity, 3.2 × 10 −2 S cm −1 at room temperature and 5.8 × 10 −2 S cm −1 at 80 °C. The second cross-linking significantly decreased the water uptake of the membrane. The performance of direct methanol fuel cell was slightly improved as compared to Nafion ® 117 due to its low methanol permeability. The results indicated that the double cros…
Methanol and proton transport through chitosan-phosphotungstic acid membranes for direct methanol fuel cell
2020
Composite chitosan-phosphotungstic acid membranes were synthesized by ionotropic gelation. Their liquid uptake is higher for thin membranes (23 ± 2 μm), while it is lower (~70%) for thicker membranes (50-70 μm). Polarization curves recorded using single module fuel cell at 70°C allowed to estimate a peak power density of 60 mW cm−2 by using 1 M as methanol and low Pt and Pt/Ru loadings (0.5 and 3 mg cm−2) at the cathode and at the anode, respectively. Electrochemical impedance spectroscopy was used to estimate the membrane conductivity and to model the electrochemical behavior of methanol electrooxidation inside the fuel cell revealing a two-step mechanism mainly responsible of overall kine…
Covalent-ionically cross-linked polyetheretherketone proton exchange membrane for direct methanol fuel cell
2010
Abstract In this paper, the proton exchange membrane prepared by covalent-ionically cross-linking water soluble sulfonated–sulfinated poly(oxa- p -phenylene-3,3-phthalido- p -phenylene-oxa- p -phenylene-oxy-phenylene) (SsPEEK-WC) is reported. Compared with covalent cross-linked PEEK-WC membrane, this covalent-ionically cross-linked PEEK-WC membrane exhibits extremely reduced water uptake and methanol permeability, but just slightly sacrificed proton conductivity. The proton conductivity of the covalent-ionically cross-linked PEEK-WC membrane reaches to 2.1 × 10 −2 S cm −1 at room temperature and 4.1 × 10 −2 S cm −1 at 80 °C. The methanol permeability is 1.3 × 10 −7 cm 2 s −1 , 10 times …
Proton Conducting Membrane Prepared by Cross-Linking Highly Sulfonated Peek for PEMFC Application
2009
The proton conducting membrane was prepared by cross-linking highly sulfonated and sulfinated poly(etheretherketone) (SsPEEK). The cross-linked membrane is low cost due to its use of non-expensive chemical and simple production procedure. The membrane exhibited high proton conductivity (0.04 S/cm at 60 °C), extremely reduced water uptake, enhanced strength and stability compared with that of non-cross-linked membrane. These results suggested that the cross-linked PEEK membrane is a suitable candidate of proton conducting membranes for polymer electrolyte membrane fuel cell (PEMFC) applications, particularly promising to be used in direct methanol fuel cell (DMFC) due to its lower methanol c…
A Covalently Cross-linked Polyetheretherketone Proton Exchange Membrane for DMFC
2009
The proton exchange membrane was prepared by covalent cross-linking sulfonated-sulfinated polyetheretherketone. The cross-linked membrane showed high proton conductivity (0.04 S/cm) with suitable water uptake, low methanol permeability (2.21 × 10-7 cm2/s) and good electrochemical stability. The results suggested that cross-linked polyetheretherketone membrane is particularly promising to be used as proton exchange membrane for the direct methanol fuel cell application.